Given their superior penetration depths, photosensitizers with longer absorption wavelengths present broader application prospects in photodynamic therapy (PDT). Herein, Ag₂S quantum dots were discovered, for the first time, to be capable of killing tumor cells through the photodynamic route by near-infrared light irradiation, which means relatively less excitation of the probe compared with traditional photosensitizers absorbing short wavelengths. On modification with polydopamine (PDA), PDA-Ag₂S was obtained, which showed outstanding capacity for inducing reactive oxygen species (increased by 1.69 times). With the addition of PDA, Ag₂S had more opportunities to react with surrounding O₂, which was demonstrated by typical triplet electron spin resonance (ESR) analysis. Furthermore, the PDT effects of Ag₂S and PDA-Ag₂S achieved at longer wavelengths were almost identical to the effects produced at 660 nm, which was proved by studies in vitro. PDA-Ag₂S showed distinctly better therapeutic effects than Ag₂S in experiments in vivo, which further validated the enhanced regulatory effect of PDA. Altogether, a new photosensitizer with longer absorption wavelength was developed by using the hitherto-unexplored photodynamic function of Ag₂S quantum dots, which extended and enhanced the regulatory effect originating from PDA.     

A post curing strategy toward the feasible covalent adaptable networks in polyacrylate latex films

The implementation of covalent adaptable networks (CANs) in general resin system is becoming attractive. In this work, we propose a simple post-curing strategy based on the core-shell structured acrylate latex for the achievement on both the improved general performance and the CANs characteristics in latex films. The building to the CANs was relied on the introduction of 4,4′-diaminophenyl disulfide as the curing agent, which cured the acetoacetoxy decorated shell polymer through the ketoamine reaction. The metathesis reaction of aromatic disulfides in the crosslinking segments enabled the thermally induced dynamic behavior of the network as revealed in the stress relaxation tests by comparison with other diamine crosslinking agents without the incorporation of disulfide. The synergism of the dynamic crosslinking of the shell polymer and static crosslinking in the core polymer contributed to the improved mechanical strength (15 MPa, strain% = 250%) and the suppressed water adsorption (~1% in 24 h of soaking) of the latex film, which exhibited above 90% of recovery in both strength and strain from a cut-off film damage within 1 h at 80°C. Moreover, the cured latex film could be recycled, and 75% of the mechanical performance was regained after three fragmentation-hot-pressing cycles. These, in addition with the feasible and environmental friendly characteristics, suggest a sustainable paradigm toward the smart thermosetting latex polymers.     

Entropic uncertainty relation in neutrino oscillations

The European Physical Journal C - We study the isentropic evolution of the matter produced in relativistic heavy-ion collisions for various values of the entropy-per-baryon ratio of interest for...     

盐酸伊达比星杂质A的合成工艺优化及其高效液相分析

通过对盐酸伊达比星脱羟基杂质A的合成研究，为盐酸伊达比星的质控标准提供参考。以盐酸伊达比星为起始原料，经过4步反应得到脱羟基杂质A。本文提供了盐酸伊达比星杂质A的制备方法以及高效液相色谱分析方法，为杂质含量控制提供了依据。该工艺可以稳定、快速制备高纯度脱羟基杂质A，制备总收率为57.20%，纯度为57.20%，其结构经¹H NMR， ¹³C NMR和MS(ESI)表征。     

均匀磁场下碳离子笔形束的剂量变化分析及位置修正方法

分析外加均匀磁场对于碳离子笔形束剂量分布的影响,并考虑修正这种影响,为磁共振成像引导碳离子放射治疗的临床应用提供指导。本文利用蒙特卡罗方法模拟计算了不同能量碳离子笔形束在不同强度磁场下的剂量分布情况,发现垂直于碳离子束入射方向的均匀磁场对于碳离子笔形束射程缩短的影响很小,磁场对碳离子束的主要影响是引起束流横向偏转,特别是碳离子束布拉格峰位置的横向侧移。横向侧移程度与碳离子束的能量和磁场强度相关,根据模拟结果,得到了一个计算碳离子束布拉格峰在磁场中相对横向偏转的方程,并提出一种校正外加磁场引起的碳离子束布拉格峰横移的角度修正方法。这些结果可用于指导磁共振图像引导碳离子放射治疗计划系统的研发。     

航空导管弯曲试验的疲劳裂纹萌生寿命

飞行器液压导管受接头和卡箍等约束，在使用的振动环境中，会因弯曲应力而导致破裂，影响到飞行安全．本文对飞行器液压系统通用的不锈钢导管的裂纹萌生寿命进行了试验研究．首先在对8 mm、12 mm 无缺陷导管和含U 型缺口8 mm 导管的疲劳试验和有限元分析的基础上，得到了导管的最大拉应变-裂纹萌生寿命数据．然后采用基于强度极限和弹性模量估算法的Manson-Coffin 公式来预测导管裂纹萌生寿命．最后引入加载类型修正系数、表面质量修正系数、试样尺寸修正系数、应力集中敏感系数和有效应力集中系数，使修正后的公式对三种类型的导管均有较好的裂纹萌生寿命预测精度．     

Eu:Lu2O3透明闪烁陶瓷的制备与性能

采用湿化学法合成了Eu原子掺量5%的Lu₂O₃陶瓷前驱体,通过SEM、XRD研究了煅烧前后前驱体和1 100 ℃煅烧4 h后粉体的形貌、结构以及物相。结果表明煅烧后的粉体为纳米类球形、高分散且结晶性良好的颗粒。颗粒尺寸为68.5 nm。使用煅烧后的粉体为原料,在1 650 ℃真空烧结30 h制备了高透过率的Eu:Lu₂O₃陶瓷,晶粒尺寸为46 μm,在611 nm处的直线透过率可以达到66.3%。此外对陶瓷的吸收曲线、光致激发和发射光谱特性以及X射线激发发射光谱进行研究。可观察到,Eu:Lu₂O₃陶瓷存在基质和激活离子两类吸收,光致发光光谱和X射线激发发射光谱均可以看出Eu:Lu₂O₃陶瓷存在极强的⁵D₀→⁷F₂跃迁发光,位于611 nm处。对比商业的BGO单晶的X射线发射光谱,可得本实验中制备的陶瓷的光输出为85 000 ph/MeV。Eu:Lu₂O₃陶瓷本身有着高X射线以及高能粒子的阻止能力,结合高光输出特性,表明Eu:Lu₂O₃陶瓷在X射线成像等领域具有巨大的潜在应用价值。